2. Aluminium Profile Processing:
________________________________________________________________
Raw material purchase--Extruding--Put in semi-finished products warehouse--after the acid and alkali chemical reation--Natural anodized--Air driving--Packaging--Saved in finished products warehouse
Chemical composition
| Alloy | Si | Mg | Fe | Cu | Mn | Zn | Cr | Ti |
| 6063 | 0.2~0.6 | 0.45~0.90 | <0.35 | <0.10 | <0.10 | <0.10 | <0.10 | <0.10 |
| | | | | | | | | |
| 6061 | 0.4~0.8 | 0.80~1.2 | <0.70 | 0.15~0.4 | <0.15 | <0.25 | 0.04~0.35 | <0.15 |
| | | | | | | | |
|
Quality Control
We operate the most strict quality control system, the detection is from the material, production process, to final product, and ensure the product quality and traceability.
The variety, state and typical use of aluminum alloy
The aluminum alloy is aluminum alloy with manganese as the main alloy, which belongs to the unreinforced aluminum alloy. Its high plasticity, good welding performance, strength is higher than 1 series aluminum alloy, and corrosion resistant performance is close to 1 series aluminum alloy, it is a kind of medium strength of the aluminum alloy corrosion resistant performance is good, it is widely used, the amount is big.
Currently, production of 3 series aluminum alloy plate number: 3003 LF21
The variety, state and typical use of aluminum alloy
4 series aluminum alloy based on silicon as the main alloying element of aluminium alloy, its most alloys are not reinforced aluminum alloy heat treatment, only including Cu, and Ni alloy, Mg and learned some after welding heat treatment strengthening alloy elements, can only through strengthening heat treatment. Department alloys due to their high silicon content, low melting point, good melt flow, easy feeding, brittleness, and not of the final product so adding material mainly used in the manufacture of aluminum alloy welding, such as soldering plate, wire electrode and candle. In addition, due to some of the piston and heat resistant parts. The alloys containing about 5% of silicon are black and gray after anodizing, so they are suitable for building materials and decorative parts.
Current production 4 series aluminum alloy number: 4032